TAROBLEND 60 X0
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m2KzKy_TAROBLEND-60-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS alloy self extinguishing UL94 V0, medium thermal resistance, improved thermal stability, low halogen content, without antimony trioxide. UL94 approved V0 all colors at 1,7 mm. UL746B approved. Available: different colours. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 to 1.21 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 to 0.60 | % | |
| Across Flow | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.30 | % | ASTM D570, ISO 62 |
| Saturation | 0.70 | % | ASTM D570 |
| Saturation, 23°C | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2750 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 65.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 40 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2550 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 90.0 | MPa | ISO 178 |
| Yield | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 22 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 3(23°C) | No Break | ASTM D256, ISO 179 | |
| Notched Izod Impact (23°C, 3.20 mm) | 450 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 88.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | 60.0 | °C | UL 746B |
| Vicat Softening Temperature | 122 | °C | ISO 306/A50, ASTM D1525 4 |
| Ball Pressure Test (75°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.70 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Pre-heater | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | 6x4x50 mm |
| 3 . | 6x4x50 mm |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1500-40D TFE 15 SI | RTP Company | TPU-Polyester | RTP |
| Sinvicomp DFR2704 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| 4POM® 9I15100 | 4Plas | Acetal (POM) Homopolymer | 4POM® |
| EPO-TEK® 320-3 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| HONES® Conductive Nylon | Guangdong Shunde Hones Polymer Material Co., Ltd. | Nylon, Unspecified | HONES® |