TRANSMARE® 14CGF30-0.001
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m20q3U_TRANSMARE-14CGF30-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 14CGF30-0.001 is a 30 % glass fiber reinforced polypropylene copolymer for injection molding purposes with high stiffness, high impact and a good flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 6.0 | g/10 min | |
| 230°C/5.0 kg | 25 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 75.0 | MPa | |
| Break, 4.00 mm | 75.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 4.5 | % | |
| Break, 4.00 mm | 6.0 | % | |
| Flexural Modulus 1 | 4900 | MPa | ISO 178 |
| Flexural Stress 2 | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -40°C | 12 | kJ/m² | |
| -20°C | 13 | kJ/m² | |
| 0°C | 15 | kJ/m² | |
| 23°C | 19 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 14 | kJ/m² | |
| -20°C | 15 | kJ/m² | |
| 0°C | 17 | kJ/m² | |
| 23°C | 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 157 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 157 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC8PAN (Series: AD/PA) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Ultraform® N 2320 003 PRO | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Clariant Nylon 6/6 66M40-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Grivory® HT1V-5 FWA black 9225 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| Sylvin 9067-80 White 1118 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |