Quadrant EPP BG PPS
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m1u3vc_Quadrant-EPP-BG-PPS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP BG PPS is a Polyphenylene Sulfide (PPS) product. It can be processed by compression molding and is available in North America. Typical application: Engineering/Industrial Parts. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.020 | % | |
| Saturation | 0.030 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 93 | ||
| R-Scale | 126 | ||
| Durometer Hardness (Shore D) | 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6760 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 14.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 5650 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 68.9 | MPa | ASTM D790 |
| Compressive Modulus | 5520 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 103 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.20 | Internal Method | |
| Wear Factor | 1600 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 254 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 232 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.876 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 282 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.32 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | < 1.0E+5 | ohms | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP2S34F | Shazand (Arak) Petrochemical Corporation | PP Random Copolymer | Moplen |
| ACRYLITE® LED 8N LD12 | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| Arnite® T06 200 (extrusion) | DSM Engineering Plastics | PBT | Arnite® |
| Lupol® GP3102Y | LG Chem Ltd. | TPO | Lupol® |
| TAFMER™ PN-20300 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |