Category: | PC , Polycarbonate |
Manufacturer: | Entec Polymers |
Trademark: | Hylex® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | m19Gp0_HylexP1010L1.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
POLYCARBONATE, CLEAR EDGE TINT |
General Information | |
---|---|
Appearance |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield, 23°C) | 70.3 | MPa | ASTM D638 |
Tensile Elongation (Break, 23°C) | 120 | % | ASTM D638 |
Flexural Modulus (23°C) | 2060 | MPa | ASTM D790 |
Flexural Strength (23°C) | 86.2 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C, 3.18 mm) | 910 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 135 | °C | ASTM D648 |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating | UL 94 | ||
1.5 mm | V-2 | UL 94 | |
3.0 mm | V-2 | UL 94 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
MELOPAS® MP 181 | RASCHIG GmbH | Mel Phenolic | MELOPAS® |
Witcom TPE 2006/562 | Witcom Engineering Plastics B.V. | TPE | Witcom TPE |
HAIPLEN H90 T4 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
Oleflex™ 6261-70A; 307105 | Vi-Chem Corporation | TPE | Oleflex™ |
LubriOne™ NN-000/15T BK204 | PolyOne Corporation | Nylon 66 | LubriOne™ |