Order Products : sales@su-jiao.com
Kelon® B FR H2 CE/25-V2HF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Kelon® B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m15Bga_Kelon-B-FR-H2-CE-25-V2HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6). Heat stabilised. Mineral filler. UL94 V-2 classified, halogens and red phosphorous free. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.65 to 0.85 | % | |
| Flow : 2.00 mm | 0.55 to 0.75 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 5200 | MPa | |
| 60°C | 2200 | MPa | |
| 90°C | 1300 | MPa | |
| 120°C | 750 | MPa | |
| 150°C | 500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 65.0 | MPa | |
| Break, 60°C | 45.0 | MPa | |
| Break, 90°C | 30.0 | MPa | |
| Break, 120°C | 20.0 | MPa | |
| Break, 150°C | 15.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.5 | % | |
| Break, 60°C | 3.5 | % | |
| Break, 90°C | 7.0 | % | |
| Break, 120°C | 12 | % | |
| Break, 150°C | 20 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 30 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 80.0 | °C | |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 750 | °C | |
| 2.00 mm | 750 | °C | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PP P840 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| ACCUTECH™ HP0334C20L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| ICORENE® N1006 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| PHOENIX™ 8301 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| ISPLEN® PR210 G4E | REPSOL | PP Random Copolymer | ISPLEN® |