ACCUTECH™ CP0437G40CL
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m0sV5Q_ACCUTECH-CP0437G40CL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™CP0437G40CL is a polypropylene copolymer (PP Copoly) product, which contains a 40% glass fiber reinforced material. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 56.0 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 8.0 | % | ASTM D638 |
| Flexural Modulus | 5500 | MPa | ASTM D790 |
| Flexural Strength | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 140 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 40% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 HI2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| CYCOLAC™ MG34LG resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| DILAMID® 6 FVT 30 NAT A | Dilaplast S.p.A. | Nylon 6 | DILAMID® |
| Karina WHITE PVC COMPOUND 808D10/173-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| CYCOLAC™ MG37EPX resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |