ADVANCENE™ EM-5420-AAH
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | ETHYDCO |
| Trademark: | ADVANCENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m0XY5Y_ADVANCENEEM5420AAH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADVANCENE™ EM-5420-AAH High Density Polyethylene (HDPE) Resin is produced via advanced gas phase PE process and is intended for use in a broad range of injection molding applications such as housewares, toys, food containers and pails. This resin has been designed to provide an excellent balance of toughness, environmental stress crack resistance and processability. Main Charactenstics :
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 3.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 57 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 28.3 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 13.8 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 7.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 250 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 2% Secant | 1150 | MPa | ASTM D790B, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | |||
| -- 1 | 42.0 | kJ/m² | ASTM D1822 |
| -- | 42.0 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 73.0 | °C | ASTM D648, ISO 75-2/B |
| Brittleness Temperature | < -76.0 | °C | ASTM D746, ISO 974 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 130 | °C | ASTM D3418, ISO 3146 |
| Peak Crystallization Temperature (DSC) | 117 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Type S |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Celanex® 733LD | Celanese Corporation | PBT | Celanex® |
| DOMAMID® 66B40 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Lifolit® SG 45.1095/1 NP | ELASTO | PVC, Flexible | Lifolit® |
| LNP™ LUBRICOMP™ RAL23S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| LTP CT-1220 | Chengdu Letian Plastics Co., Ltd | PPS | LTP |