| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m03clA_CERTENELDF219A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-219A is a certified prime resin specially designed to meet the requirements of most 1 to 3 mils thickness Blown film liner applications. LDF-219A features easy processability. Large lot size and superior lot-to-lot uniformity ensure consistent film production. Minimum recommended film thickness is 1.0 mil. LDF-219A contains no slip and no antiblock. LDF-219A complies with FDA regulation 21CFR 177.1520 (c) 2.1 + 2.2 and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm | 175 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm | 205 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 25.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 19.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 350 | % | ASTM D882 |
| TD : Fracture, 38 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (38 µm) | 85 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 580 | g | ASTM D1922 |
| TD : 38 µm | 120 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 10 | ASTM D2457 | |
| Haze | 5.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO T1202 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Edgetek™ X ET9800-0030 RS Natural | PolyOne Corporation | PEEK | Edgetek™ |
| INLUBE INX-TPU-05140 | Infinity LTL Engineered Compounds | TPU, Unspecified | INLUBE |
| Karina CLEAR PVC COMPOUND 65/205-DA-IS-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OTECH ALLOY NT1000-60 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |