Mecoline I RDX 1201 F
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Melos GmbH |
| Trademark: | Mecoline |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lysWOW_Mecoline-I-RDX-1201-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A flame retardant, halogen-free and low smoke, oil resistant compound. Max. operating temperature 125°C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Wire Types |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (160°C/21.6 kg) | 8.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 45 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 811-1-1 | ||
| -- 1 | 18.0 | MPa | |
| -- 2 | 11.5 | MPa | |
| Tensile Strain | IEC 811-1-1 | ||
| Break 3 | 210 | % | |
| Break 4 | 230 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 811-1-2 | ||
| 155°C, 1008 hr | 20 | % | |
| 165°C, 480 hr | 11 | % | |
| 180°C, 144 hr | 5.9 | % | |
| Change in Tensile Strain at Break in Air | IEC 811-1-2 | ||
| 155°C, 1008 hr | -21 | % | |
| 165°C, 480 hr | -25 | % | |
| 180°C, 144 hr | -20 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressure Test - penetration 4h at 140°C | 8.0 | % | IEC 811-3-1 |
| Hot Set 5 | IEC 540 | ||
| Elongation after unloading | 10 | % | |
| Elongation under load | 25 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 180 to 200 | °C | |
| Extruder Screw L/D Ratio | 20.0:1.0 to 25.0:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 6 | IEC 60093 | ||
| 23°C | 3.5E+14 | ohms·cm | |
| 90°C | 6.6E+11 | ohms·cm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 30 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 140 to 160 | °C | |
| Cylinder Zone 2 Temp. | 150 to 170 | °C | |
| Cylinder Zone 3 Temp. | 170 to 190 | °C | |
| Cylinder Zone 4 Temp. | 175 to 195 | °C | |
| Cylinder Zone 5 Temp. | 180 to 200 | °C | |
| Adapter Temperature | 180 to 200 | °C | |
| Die Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | After crosslinking |
| 2 . | Before crosslinking |
| 3 . | After crosslinking |
| 4 . | Before crosslinking |
| 5 . | at 200°C/15min/0.2 MPa |
| 6 . | 500V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 HB | RTP Company | ABS | RTP |
| Santron IMS2007LF | Bhansali Engineering Polymers Limited | SAN | Santron |
| RTP 103 AV (20% FOAMED) | RTP Company | PP, Unspecified | RTP |
| Shin-Etsu Elastomer KE-2095-60A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Vi-Chem PVC V221-87E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |