LNP™ THERMOCOMP™ 5C004 compound
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ly4gpa_LNP-THERMOCOMP-5C004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 5C004 is a compound based on Polyvinylidene Fluoride resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound FP-VC-1004 Product reorder name: 5C004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 16400 | MPa | ASTM D638 |
| Tensile Strength (Break) | 84.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 13900 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 290 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 154 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 210 to 225 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 215 to 230 | °C | |
| Mold Temperature | 65.0 to 90.0 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 G4 X0 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Topilene® J640F | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| XANTAR® 25 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Colorite CS Series CS7566LS | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Flontech® FT-1-1F | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |