KumhoSunny PA/PPE HAP8940
| Category: | Nylon+PPE , Polyamide + PPE |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PA/PPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lxyVle_KumhoSunny-PA-PPE-HAP8940.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HAP8940 is an unreinforced PA66/PPE alloy, with excellent chemical resistance, paintability and high impact. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 1.1 to 1.5 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 62.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 80 | % | ISO 527-2/50 |
| Flexural Modulus 1(64.0 mm) | 2190 | MPa | ISO 178 |
| Flexural Stress 2(64.0 mm) | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 41 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 5 | ISO 180 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 37 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | ISO 180 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed | 175 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 190 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Condition: 4 J |
| 4 . | Condition: 4 J |
| 5 . | Condition: 5.5 J |
| 6 . | Condition: 5.5 J |
| 7 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Karina IVORY PVC COMPOUND 105900-35/ 1-B-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petlon R-Prime A2-00-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon R-Prime |
| Hifax CB 1160 G1 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |
| OTECH TPE OTR6988 - Profile | OTECH Corporation | TPE | OTECH TPE |
| Starex PT-0170 M | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |