Clariant Nylon 6/6 PA-113M40W
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6/6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lwpYlZ_Clariant-Nylon-6-6-PA-113M40W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant Nylon 6/6 PA-113M40W is a Polyamide 66 (Nylon 66) material filled with 40% mineral. It is available in North America for injection molding. Primary attribute of Clariant Nylon 6/6 PA-113M40W: Flame Rated. Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 95 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 5860 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 249 | °C | |
| 1.8 MPa, Unannealed | 238 | °C | |
| Melting Temperature | 256 | °C | |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 266 to 293 | °C | |
| Middle Temperature | 266 to 293 | °C | |
| Front Temperature | 266 to 293 | °C | |
| Processing (Melt) Temp | 266 to 288 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versalloy™ HC 9220-70 | PolyOne Corporation | TPE | Versalloy™ |
| VYPET VNT 645 | Lavergne Group | PET | VYPET |
| CP PRYME® Polypropylene PPH100-4M | Chase Plastics Services Inc. | PP Homopolymer | CP PRYME® Polypropylene |
| HiFill FR® PA6/6 GF25 FR-N IM BK | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |
| Iupital® ET-25 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |