PRE-ELEC® PP 1351
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lweYOI_PRE-ELEC-PP-1351.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PP 1351 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resistance between 10e5-10e8 ohms. PRE-ELEC® PP 1351 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include injection moulded dissipative ESD products such as crates, boxes and tote bins. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.996 | g/cm³ | ASTM D792 |
| -- | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 6.0 | g/10 min | |
| 230°C/5.0 kg | 28 | g/10 min | |
| Molding Shrinkage - Flow | 1.2 to 1.8 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A | 98 | ||
| Shore D | 74 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 25.0 | MPa | ASTM D638, ISO 527-2 |
| -- | 22.0 | MPa | ASTM D638 |
| 4.00 mm | 22.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break, 4.00 mm | 10 | % | |
| Flexural Modulus | |||
| 4.00 mm | 1380 | MPa | ASTM D790 |
| 4.00 mm | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 2.1 | kJ/m² | ASTM D256 |
| -20°C | 2.0 | kJ/m² | ISO 179 |
| 23°C | 9.0 | kJ/m² | ISO 179 |
| 23°C | 8.4 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | 32 | kJ/m² | ASTM D256, ISO 179 |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 2.10 | kJ/m² | |
| 23°C, 4.00 mm | 8.41 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 21.0 | kJ/m² | |
| 23°C, 4.00 mm | No Break | ||
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | 20 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 83.9 | °C | ASTM D648B |
| 0.45 MPa, Unannealed | 84.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 47.8 | °C | ASTM D648A |
| 1.8 MPa, Unannealed | 48.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ASTM D1525, ISO 306/A50 3 5 |
| -- | 82.2 | °C | ASTM D1525 6 |
| -- | 82.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+8 | ohms | IEC 61340-2-3 |
| Volume Resistivity | 1.0E+3 to 1.0E+7 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 80.0 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PE GM 5010 T2 B | Braskem | HDPE | Braskem PE |
| Appeel® 1181 | DuPont Packaging & Industrial Polymers | EVA | Appeel® |
| Epolene® C-17P | Westlake Chemical Corporation | LDPE | Epolene® |
| Hostacom NXK91201 | LyondellBasell Industries | TPO (POE) | Hostacom |
| ADLEN® G08BGD00 | A.D. Compound S.p.A. | PP Copolymer | ADLEN® |