SABIC® SUPEER™ 8112
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® SUPEER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lwCWIa_SABICSUPEER8112.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® SUPEER™ 8112 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has good processablity. Application Typical applications for SABIC® SUPEER™ 8112 are lamination film, frozen bags, liquid pouches, industrial liner, stretch hood, surface protective film. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.912 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 50 µm, blown film | 127 | MPa | ASTM D882 |
| 1% secant, TD : 50 µm, blown film | 142 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 51.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 49.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 660 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 730 | % | ASTM D882 |
| Dart Drop Impact 1(50 µm, Blown Film) | > 1000 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 16 | g | ASTM D1922 |
| TD : 50 µm, blown film | 25 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 111 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blown Film Melt Temperature | 180 - 200 | °C | |
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured on blown film of 50 µm and BUR = 2.5 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® P PN0W | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| Aropol™ Q 67700 INF | Ashland Performance Materials | Polyester, TS | Aropol™ |
| DI-COAT R-4721/30 | Hapco Inc. | TP, Unspecified | DI-COAT |
| Gravi-Tech™ GT6000-5002 White FD | PolyOne Corporation | Nylon 6 | Gravi-Tech™ |
| Sylvin 8980-88 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |