ALCUDIA® HDPE TR-156
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lvot3G_ALCUDIA-HDPE-TR-156.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® TR156 is a high density polyethylene film grade, which combines superior physical properties with excellent processability. Due to high density, the material properties are best utilised by processing at HDPE conditions. Film made of ALCUDIA® TR-156 has good strength, high stiffness, impact and balanced tear resistance. It contains antioxidant additives. TYPICAL APPLICATIONS
ALCUDIA® TR-156 is intended for high neck extrusion on HDPE film extruders. The material will provide optimal performance in extrusion and mechanical properties. Recommended extrusion conditions are flat temperature profile with a melt temperature between 210 and 230°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.956 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.30 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 9.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 15 µm, blown film | 50.0 | MPa | ISO 527-3 |
| TD : Broken, 15 µm, blown film | 55.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 15 µm, blown film | 250 | % | ISO 527-3 |
| TD : Broken, 15 µm, blown film | 300 | % | ISO 527-3 |
| Dart Drop Impact (15 µm, Blown Film) | 350 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 15 µm, blown film | 0.20 | N | ISO 6383-2 |
| TD : 15 µm, blown film | 0.30 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 127 | °C | ISO 306/A |
| Melting Temperature | 133 | °C | ISO 11357-3 |
| Additional Information |
|---|
| Data taken from 15 µm film sample produced in a 65 mm extruder, die 160 x 1,5mm, BUR = 4:1, neck = 8 x die diameter. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 71 GF 10 | Plastcom | PP, Unspecified | SLOVALEN® |
| Axiall PVC 8791 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Chemisat® LCH-7302X | Zeon Chemicals L.P. | NBR | Chemisat® |
| Ferro PP LPP40BC93HB WHITE | Ferro Corporation | PP Homopolymer | Ferro PP |
| Jam PE 20505 | Jam Petrochemical Company | LLDPE | Jam PE |