LNP™ LUBRICOMP™ KAL22M compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lvg4iV_LNP-LUBRICOMP-KAL22M-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* KAL22M is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KAL-4022 M Product reorder name: KAL22M |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.40 | g/cm³ | |
| -- | 1.45 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.21 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2870 | MPa | ASTM D638 |
| -- | 2590 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 41.0 | MPa | ASTM D638 |
| Break | 39.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 8.5 | % | ASTM D638 |
| Yield | 8.8 | % | ISO 527-2/5 |
| Break 4 | 14 | % | ASTM D638 |
| Break | 14 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 2430 | MPa | ASTM D790 |
| -- 6 | 2420 | MPa | ISO 178 |
| Flexural Stress | 62.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.23 | ||
| vs. Itself - Static | 0.16 | ||
| Wear Factor - Washer | 8.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 36 | J/m | ASTM D256 |
| 23°C 7 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 370 | J/m | ASTM D4812 |
| 23°C 8 | 26 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.00 | J | ASTM D3763 |
| -- | 1.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 155 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 147 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 94.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 84.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.0E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 20GF GWT 960 | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Shanghai Ofluorine PVDF 9203 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| DOWLEX™ NG 5056G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Durez® 33681 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| PolyFibra® PF-PEF05 | FuturaMat | PP, Unspecified | PolyFibra® |