LNP™ THERMOCOMP™ MF002S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | luhwlq_LNPTHERMOCOMPMF002Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP MF002S is a compound based on Polypropylene resin containing Glass Fiber. Added features include: Heat Stabilized. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 53.0 | MPa | ISO 527-2/5 |
| Fracture | 51.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 4.0 | % | ISO 527-2/5 |
| Fracture | 4.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 145 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 106 | °C | ISO 75-2/Af |
| CLTE - Flow (23 to 60°C) | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 216 - 227 | °C | |
| Front Temperature | 238 - 249 | °C | |
| Processing (Melt) Temp | 227 - 249 | °C | |
| Mold Temperature | 32.2 - 48.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2667 | Covestro - Polycarbonates | PC | Makrolon® |
| Sarlink® TPV 3460N | Teknor Apex Company | TPV | Sarlink® TPV |
| Vibrathane® B600 | Chemtura | PUR-Ether/TDI | Vibrathane® |
| Nanjing Hongrui PBT T304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| FLEXAREN® 18020 | Innospec Leuna GmbH | EVA | FLEXAREN® |