Edgetek™ QT-20MN/000 natural HI
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | luarLN_Edgetek-QT-20MN-000-natural-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edgetek™ QT-20MN/000 natural HI is a Syndiotactic Polystyrene (SPS) product filled with mineral\inorganic. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow 1(23°C, 4.00 mm, Injection Molded) | < 1.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(23°C) | 4200 | MPa | ISO 527 |
| Tensile Strength 3(Break, 23°C) | 50.0 | MPa | ISO 527 |
| Tensile Elongation 4(Break, 23°C) | 1.5 | % | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 230 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 270 to 320 | °C | |
| Mold Temperature | 80.0 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | Bergmann Method |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitalac® 5000S | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| YUNGSOX® PP 3204 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| AKROLOY® PA GF 60 natural (2941) | AKRO-PLASTIC GmbH | Nylon 66+Nylon 6I/6T | AKROLOY® |
| Elastollan® C90A | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |
| INEOS PP 401-NA01 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | INEOS PP |