LNP™ LUBRICOMP™ DFL36 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lteg7U_LNPLUBRICOMPDFL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DFL-4036 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound DFL-4036 Product reorder name: DFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 8.00 - 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.10 - 0.30 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus 2 | ISO 178 | ||
| -- | 8600 | MPa | ISO 178 |
| 60°C | 8400 | MPa | ISO 178 |
| 100°C | 8100 | MPa | ISO 178 |
| 120°C | 7500 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 199 | MPa | ISO 178 |
| 60°C | 172 | MPa | ISO 178 |
| 100°C | 136 | MPa | ISO 178 |
| 120°C | 114 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.45 | ASTM D3702 Modified | |
| With Self-Static | 0.41 | ASTM D3702 Modified | |
| Flexural Strain at Break 3 | ISO 178 | ||
| -- | 3.1 | % | ISO 178 |
| 60°C | 3.1 | % | ISO 178 |
| 100°C | 3.5 | % | ISO 178 |
| 120°C | 3.8 | % | ISO 178 |
| Wear Factor - Washer | 22.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C) | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 130 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 7.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STRANOX PA6/ST/45%LFT | Oxford Polymers | Nylon 6 | STRANOX |
| Cereplast Hybrid Resins® 101 | Cereplast, Inc. | PP Alloy | Cereplast Hybrid Resins® |
| HANWHA LLDPE 4200 | Hanwha Chemical | LLDPE | HANWHA LLDPE |
| INSULCAST® RTVS 3-95-1 | ITW Polymers Coatings North America | Silicone Rubber, RTV-2 | INSULCAST® RTVS |
| OXNILON 6 30GF | Oxford Polymers | Nylon 6 | OXNILON 6 |