Sarlink® TPE FM-2676B BLK XRD4 (DISCONTINUED)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lrnvGb_SarlinkTPEFM2676BBLKXRD4DISCONTINUED.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| THIS GRADE IS DISCONTINUED - PLEASE CONTACT YOUR TEKNOR APEX REP FOR MORE INFO |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 77 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 75 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance | ASTM D1044 | ||
| 1000 Cycles, 1000g, H-18 wheel | 6.00 | mg | ASTM D1044 |
| 2000 Cycles, 1000g, H-18 runner | 16.0 | mg | ASTM D1044 |
| 1000 Cycles, 1000g, H-22 wheel | 28.0 | mg | ASTM D1044 |
| 2000 Cycles, 1000g, H-22 runner | 62.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 2.38 | MPa | ISO 37 |
| Flow : 100% strain | 5.28 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 8.76 | MPa | ISO 37 |
| Flow : Fracture | 5.81 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 730 | % | ISO 37 |
| Flow : Fracture | 200 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 33 | kN/m | ISO 34-1 |
| Flow | 39 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 24 | % | ISO 815 |
| 70°C, 22 hr | 38 | % | ISO 815 |
| 90°C, 70 hr | 53 | % | ISO 815 |
| 125°C, 70 hr | 71 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -5.7 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 6.2 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | 10 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | 13 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | 1.3 | % | ISO 188 |
| Flow : 125°C, 168 hr | 7.2 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | 12 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | 14 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -1.7 | % | ISO 188 |
| Flow : 110°C, 1008 hr | -24 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -1.4 | % | ISO 188 |
| Flow : 125°C, 168 hr | -30 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| Shao A, 110°C, 1008 hr 8 | 3.7 | ISO 188 | |
| Shao A, 110°C, 1008 hr 9 | 3.3 | ISO 188 | |
| Shao A, 110°C, 1008 hr 10 | 2.5 | ISO 188 | |
| Shao A, 125°C, 168 hr 11 | 3.8 | ISO 188 | |
| Shao A, 125°C, 168 hr 12 | 3.3 | ISO 188 | |
| Shao A, 125°C, 168 hr 13 | 1.7 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 313 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35 - 66 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 15 sec |
| 9 . | 5 sec |
| 10 . | 1 sec |
| 11 . | 15 sec |
| 12 . | 5 sec |
| 13 . | 1 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PE 2009/271 | Witcom Engineering Plastics B.V. | PE, Unspecified | Witcom PE |
| NEXT REPROCESSED POMC M90-100R | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REPROCESSED |
| Andur M-11 (94% 1,4BD, 6% TMP) | Anderson Development Company | PUR-Ester/MDI | Andur |
| Fainplast PVC PH 58/AL | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Infino XP-2140C | SAMSUNG SDI CO., LTD. | PPS | Infino |