Trithene® TS 7045
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Trithene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lrgHsD_Trithene-TS-7045.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trithene®TS 7045 is a low density polyethylene material,. This product is available in Latin America and is processed by film extrusion. Trithene®The main features of TS 7045 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 10.0 | MPa | ASTM D638 |
| Fracture, molding | 12.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 540 | % | ASTM D638 |
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.090 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 90.0 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 99.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 18.5 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 15.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 350 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 650 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 130 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 600 | g | ASTM D1922 |
| TD : 50 µm, blown film | 330 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45, 50.0 µm, blown film | 63 | ASTM D2457 | |
| 60, 50.0 µm, blown film | 105 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 8.8 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 4.0 to 5.0 g/10 minDensity, ASTM D1505: 0.922 to 0.925 g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 - 150 | °C | |
| Cylinder Zone 2 Temp. | 145 - 160 | °C | |
| Cylinder Zone 3 Temp. | 150 - 165 | °C | |
| Adapter Temperature | 160 - 175 | °C |
| Extrusion instructions |
|---|
| Recommended Blow Up Ratio: 2-3.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-6300T | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Chemlon® 110 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| PEARLSTICK® 45-60/08 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |
| Optix® CA-8125 | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |
| TOLEN H038 TF/2 | SIBUR | PP Homopolymer | TOLEN |