Hytrel® 5526

Category:	TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER
Manufacturer:	DuPont Performance Polymers
Trademark:	Hytrel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lqiyf6_Hytrel-5526.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
55 Shore D High Performance High Flow Polyester Elastomer Developed for Injection Molding

General Information
Additive	UV Stabilizer
Agency Ratings	UL Unspecified Rating
Forms	Pellets
Processing Method	Injection Molding Thermoforming
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (TPE) (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
Part Marking Code (ISO 11469)	>TPC-ET<
Resin ID (ISO 1043)	TPC-ET

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (220°C/2.16 kg)	18	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (220°C/2.16 kg)	16.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Across Flow	1.4	%
Flow	1.4	%
Water Absorption
24 hr	0.60	%	ASTM D570
23°C, 24 hr, 2.00 mm	0.60	%	ISO 62
Equilibrium, 23°C, 2.00 mm, 50% RH	0.20	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Shore Hardness			ISO 868
Shore D	55
Shore D, 15 sec	51

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	190	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Yield	14.0	MPa
Break	43.0	MPa
5.0% Strain	6.90	MPa
10% Strain	11.0	MPa
50% Strain	14.0	MPa
Tensile Strain			ISO 527-2
Yield	37	%
Break	> 300	%
Nominal Tensile Strain at Break	780	%	ISO 527-2
Tensile Creep Modulus			ISO 899-1
1 hr	170	MPa
1000 hr	130	MPa
Flexural Modulus	200	MPa	ISO 178
Abrasion Resistance	120	mm³	ISO 4649

Fill Analysis	Nominal Value	Unit
Specific Heat Capacity of Melt	2110	J/kg/°C
Thermal Conductivity of Melt	0.19	W/m/K

Additional Information	Nominal Value	Unit
Effective Thermal Diffusivity	0.0544	cSt

Elastomers	Nominal Value	Unit	Test Method
Tear Strength			ISO 34-1
Across Flow	130	kN/m
Flow	130	kN/m

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-40°C	30	kJ/m²
-30°C, Partial Break	150	kJ/m²
23°C	No Break
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break
23°C	No Break
Tensile Impact Strength (23°C)	200	kJ/m²	ISO 8256/1

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	65.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	45.0	°C	ISO 75-2/A
Brittleness Temperature	-98.0	°C	ISO 974
Glass Transition Temperature ¹	-20.0	°C	ISO 11357-2
Vicat Softening Temperature
--	180	°C	ISO 306/A50
--	75.0	°C	ISO 306/B50
Melting Temperature ²	203	°C	ISO 11357-3
CLTE			ISO 11359-2
Flow	2.0E-4	cm/cm/°C
Transverse	1.9E-4	cm/cm/°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity	4.0E+13	ohms·cm	IEC 60093
Electric Strength	20	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	4.90
1 MHz	4.60
Dissipation Factor			IEC 60250
100 Hz	9.0E-3
1 MHz	0.038
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Burning Rate ³(1.00 mm)	28	mm/min	ISO 3795
Flammability Classification			IEC 60695-11-10, -20
1.50 mm	HB
3.00 mm	HB
Oxygen Index	21	%	ISO 4589-2

Fill Analysis	Nominal Value	Unit
Melt Density	1.04	g/cm³

Note Message
1 .	10°C/min
2 .	10°C/min
3 .	SE/B

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P3967H	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
TARODUR 100 X0	Taro Plast S.p.A.	ABS	TARODUR
Wellamid® MRT1487 N	Wellman Engineering Resins	Nylon 66	Wellamid®
LTP ZC-2602 CF 30%	Chengdu Letian Plastics Co., Ltd	TP, Unspecified	LTP
KMI PP KM-5161H	KMI Group, Inc.	PP Homopolymer	KMI PP