HAIPLEN H90 T4
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lqirge_HAIPLEN-H90-T4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HAIPLEN H90 T4 is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.1 | % | ASTM D955 |
| Transverse flow | 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 40 | % | ASTM D638, ISO 527-2 |
| Flexural Stress | |||
| -- | 50.0 | MPa | ISO 178 |
| Fracture | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A50 1 1 |
| -- | 85.0 | °C | ASTM D1525, ISO 306/B50 2 2 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact Strength , ISO 180, 23°C: 30 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h), 压 力1 (10N) |
| 2 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP210G | LyondellBasell Industries | PP Random Copolymer | Moplen |
| XENOY™ X5100 resin | SABIC Innovative Plastics Europe | PC+Polyester | XENOY™ |
| CYCOLAC™ MG94 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Ducor® 1084K | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| RTP 2099 X 138791 | RTP Company | PC+PBT | RTP |