Cevian®-V 520, 520SF
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lpgmk0_Cevian--V-520-520SF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cevian®-V 520, 520SF is an acrylonitrile butadiene styrene (ABS) material,. This product is available in the Asia-Pacific region,. Cevian®The main characteristics of-V 520, 520SF are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 55.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 30 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 12.7mm | 92.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 81.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 190 - 210 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Back Pressure | 10.0 - 20.0 | MPa | |
| Screw Speed | 70 - 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLOY® UB-0010N G50N4N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Nycal™ 2120H Bk-7 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| Centrex® 814 | Network Polymers, Inc. | ASA | Centrex® |
| HiFill® PA6/6 LGF60 HS L UV 12mm | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Karina CLEAR PVC COMPOUND 65/213 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |