EXCELLOY CK10G20
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | EXCELLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | logyzP_EXCELLOY-CK10G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EXCELLOY CK10G20 is a Polycarbonate + ABS (PC+ABS) product filled with 20% glass fiber. It can be processed by injection molding and is available in Asia Pacific or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.10 to 0.30 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 112 | ASTM D785 | |
| R-Scale | 109 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 83.4 | MPa | ASTM D638 |
| Yield | 76.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5300 | MPa | ASTM D790 |
| -- | 4910 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 118 | MPa | ASTM D790 |
| -- | 117 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | ISO 179 |
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 123 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 240 to 280 | °C | |
| Middle Temperature | 240 to 280 | °C | |
| Front Temperature | 240 to 280 | °C | |
| Mold Temperature | 50.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mecoline IS RDX 1218 F | Melos GmbH | TP, Unspecified | Mecoline |
| SCANAMID 66 A12^ QF2515 | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Allen E3400 | SEKISUI Polymer Innovations, LLC | TPO (POE) | Allen |
| Lion Idemitsu Composites PPS G561F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Sylvin 9067-80 Yellow 4147 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |