Hostaform® C 9021 MD is a special modified Polyacetal copolymer based on Hostaform® C 9021 for parts, which should be identified by metal detectors. Preliminary Datasheet |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 58.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 9.5 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.4 | kJ/m² | |
| 23°C | 4.5 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 95 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 97.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Screw L/D Ratio | 15.0:1.0 to 25.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAPEEK MG black | Röchling Sustaplast SE & Co. KG | PEEK | SUSTAPEEK |
| Andur 9200 AP | Anderson Development Company | PUR-Ether/TDI | Andur |
| Latene® 22H2 MX/25 | LATI S.p.A. | PP Homopolymer | Latene® |
| Sumiliteresin® PR-50869 | SBHPP | Phenolic | Sumiliteresin® |
| LNP™ LUBRICOMP™ KG002 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |