Moplen HP568S
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lmczPf_Moplen-HP568S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lyondellbasell Australia's Polyproylene grade HP568S is a very high flow homopolymer with a modified molecular weight distribution. HP568S can be used in the melt spinning process for the production of fine denier spunbond non-woven articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 38 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 1 sec) | 73 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 2.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 70.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 151 | °C | ISO 306/A50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 238 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| TRIBIT® EF1550GN30 | Samyang Corporation | PBT | TRIBIT® |
| Niuk 20GP17 | Shanghai Niuk New Plastic Technology Co., Ltd. | ABS | Niuk |
| NuSil CV1-2964 | NuSil Technology | Silicone | NuSil |
| Karina CLEAR PVC COMPOUND -E 75/218-D-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |