Ultramid® Structure A3WG13 LFX BK23215
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lmWQs6_UltramidStructureA3WG13LFXBK23215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid Structure A3WG13 LFX BK23215 is a 65% long glass-fiber reinforced and heat aging resistant injection molding grade designed for applications requiring excellent strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.78 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.62 | -- | % | ISO 294-4 |
| Flow | 0.39 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 23300 | 18200 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 260 | 190 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.6 | 1.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 22500 | 18900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 430 | 330 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 53 | 47 | kJ/m² | ISO 179 |
| 23°C | 40 | 38 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 82 | 74 | kJ/m² | ISO 179 |
| 23°C | 75 | 80 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 255 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Injection Pressure | 3.50 - 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203B GB 20 HS UV | RTP Company | Nylon 610 | RTP |
| Sumitomo PP FY4012E | Sumitomo Chemical Asia | PP Homopolymer | Sumitomo PP |
| VAMPLUB F 00U 44TFGr | Vamp Tech | PPS | VAMPLUB |
| ALAMID® 6.6 GF 30 MOD WL SCHWARZ-9665 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| Zytel® PLUS PLS90G30DR BK099 | DuPont Performance Polymers | Nylon 66 | Zytel® PLUS |