Iupital® F30-03
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lmEAll_Iupital-F30-03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupital® F30-03 is an Acetal (POM) Copolymer material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupital® F30-03 are:
Typical application of Iupital® F30-03: Automotive |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 27 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 23.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.00 mm) | 2.0 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 64.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.5 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 25 | % | ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 150 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 156 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| Melting Temperature | 166 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 32 | kV/mm | |
| 3.00 mm | 19 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 7.0E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 180 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 180 to 210 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 50.0 to 100 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 80 to 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAKETON NV | A. Schulman Europe | PK-Aliphatic | SCHULAKETON |
| BJB Polyurethane TC-808 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| BIOPLAST® GS 2189 | BIOTEC GmbH & Co. KG | TP, Unspecified | BIOPLAST® |
| Colorite Rigid PVC 1124-03 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| LEXAN™ SFX173RU resin | SABIC Innovative Plastics | PC | LEXAN™ |