Generic Nylon 66 - Glass Fiber, Long
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | llzHCF_Generic-Nylon-66---Glass-Fiber-Long.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Glass Fiber, Long This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.35 - 1.72 | g/cm³ | ASTM D792 |
| 23°C | 1.41 - 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.14 - 0.31 | % | ASTM D955 |
| Transverse flow : 23°C | 0.19 - 0.81 | % | ASTM D955 |
| 23°C | 0.18 - 0.81 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 9.8E-3 - 0.97 | % | ASTM D570 |
| 23°C, 24 hr | 0.80 - 0.90 | % | ISO 62 |
| Saturated, 23°C | 3.4 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.0 - 1.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 10200 - 23200 | MPa | ASTM D638 |
| 23°C | 11700 - 23300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 150 - 252 | MPa | ASTM D638 |
| Yield, 23°C | 150 - 278 | MPa | ISO 527-2 |
| Fracture, 23°C | 172 - 270 | MPa | ASTM D638 |
| Fracture, 23°C | 203 - 276 | MPa | ISO 527-2 |
| 23°C | 181 - 252 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.9 - 2.5 | % | ASTM D638 |
| Yield, 23°C | 1.7 - 2.1 | % | ISO 527-2 |
| Fracture, 23°C | 1.5 - 2.5 | % | ASTM D638 |
| Fracture, 23°C | 1.6 - 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 7890 - 21400 | MPa | ASTM D790 |
| 23°C | 10000 - 19000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 242 - 430 | MPa | ASTM D790 |
| 23°C | 243 - 437 | MPa | ISO 178 |
| Coefficient of Friction | 0.39 - 0.40 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 - 45 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 59 - 110 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 84 - 510 | J/m | ASTM D256 |
| 23°C | 19 - 55 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 530 - 1600 | J/m | ASTM D256 |
| 23°C | 51 - 100 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 8.60 - 18.0 | J | ASTM D3763 |
| 23°C | 5.60 - 20.2 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 226 - 260 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 252 - 265 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 241 - 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 250 - 263 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 234 - 241 | °C | ISO 75-2/C |
| Melting Temperature | 260 - 261 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 1.8E-5 - 1.9E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.7E-5 - 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.6E-5 - 6.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 5.3E-5 - 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp | 109 - 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 - 2.5E+12 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 82.9 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.20 | % | |
| Rear Temperature | 287 - 288 | °C | |
| Middle Temperature | 293 - 294 | °C | |
| Front Temperature | 293 - 294 | °C | |
| Nozzle Temperature | 271 - 315 | °C | |
| Processing (Melt) Temp | 295 - 296 | °C | |
| Mold Temperature | 88.9 - 105 | °C | |
| Injection Pressure | 6.89 - 135 | MPa | |
| Holding Pressure | 64.8 - 70.0 | MPa | |
| Back Pressure | 0.258 - 0.289 | MPa | |
| Screw Speed | 44 - 45 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Glass Fiber, LongThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PC 2L1 | Witcom Engineering Plastics B.V. | PC | Witcom PC |
| Xuchuan 2000/B-8580 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Polidiemme® G/430 | Solvay Specialty Polymers | TSE | Polidiemme® |
| OTECH PVC OC6014-Soles | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Geon™ Vinyl Flexible HC17080 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |