LubriOne™ NN-20CF/15T-02S BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lle1Sn_LubriOne-NN-20CF-15T-02S-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1(23°C, 4.00 mm) | 0.10 to 0.20 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(23°C, 4.00 mm) | 16500 | MPa | ISO 527 |
| Tensile Strength 3(Break, 23°C, 4.00 mm) | 160 | MPa | ISO 527 |
| Tensile Elongation 4(Break, 23°C, 4.00 mm) | 1.0 to 2.0 | % | ISO 527 |
| Flexural Modulus | 12000 | MPa | ISO 178 |
| Flexural Strength | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 245 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity (2.00 mm) | 1.0E+3 to 1.0E+6 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 288 to 299 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | bergmann method |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Suprel® SVA 9301 | Axiall Corporation | PVC, Rigid | Suprel® SVA |
| Velocity® LGF60-PA6 | PlastiComp, Inc. | Nylon 6 | Velocity® |
| Petrotene® PP A3 T35 PRTA011 PH355 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Plaslube® NY-1/SI/5 NAT | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Sylvin 9940-55 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |