HANWHA EVA 2030
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lkSeMg_HANWHA-EVA-2030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA EVA 2030 is manufactured by DOW tubular high pressure process and designed for variety of film application such as multiplayer agricultural film. EVA 2030 has well balanced property of high clarity, mechanical property and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.927 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 6.5 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 18.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 740 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 60 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 60 µm | 25.5 | MPa | ASTM D882 |
| TD : Break, 60 µm | 23.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 60 µm | 350 | % | ASTM D882 |
| TD : Break, 60 µm | 650 | % | ASTM D882 |
| Dart Drop Impact (60 µm) | > 400 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 60.0 µm | 83.4 | kN/m | ASTM D1004 |
| TD : 60.0 µm | 88.3 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 83.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 101 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (60.0 µm) | 4.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 140 - 180 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.05 to 0.1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP CESTICOLOR HD 500 | Quadrant Engineering Plastic Products | HMWPE | Quadrant EPP |
| Mirakutoran® TPU E660MZAA | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| VITAMIDE® AI10BK6201/2C | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| GELOY™ FXW710SK resin | SABIC Innovative Plastics Europe | ASA | GELOY™ |
| Iupilon® EHR3100 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |