SCHULAMID® 6 GF 30 FR 2 BLACK HL3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lkD3xS_SCHULAMID6GF30FR2BLACKHL3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fibre reinforced flame-retardant Polyamide 6 grade; halogen free |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.44 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10800 | 7500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 160 | 105 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 56 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 70 | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 209 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 216 | -- | °C | ISO 306/A50 |
| -- | 212 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (200°C) | Pass | -- | IEC 60695-10-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 475 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | ISO 3795 | |||
| 0.750mm, automatic fire extinguishing | 0.0 | -- | mm/min | ISO 3795 |
| 1.50mm, automatic fire extinguishing | 0.0 | -- | mm/min | ISO 3795 |
| 3.00mm, automatic fire extinguishing | 0.0 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.75 mm | V-0 | -- | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | -- | IEC 60695-11-10, -20 | |
| 3.0 mm | V-0 | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.75 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.5 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.0 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.75 mm | 750 | -- | °C | IEC 60695-2-13 |
| 1.5 mm | 750 | -- | °C | IEC 60695-2-13 |
| 3.0 mm | 750 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 35 | -- | % | ISO 4589-2 |
| Smoke Toxicity | 0.540 | -- | NF X70-100 | |
| Smoke Density | ISO 5659-2 | |||
| 1.00 mm | 280 | -- | ISO 5659-2 | |
| 1.60 cm | 100 | -- | ISO 5659-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec | ||
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Hopper Temperature | 70 | °C | |
| Rear Temperature | 240 | °C | |
| Middle Temperature | 255 | °C | |
| Front Temperature | 270 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 80.0 - 140 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 40.0 - 85.0 | MPa | |
| Back Pressure | 2.00 - 8.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® E 8901A | Vyncolit N.V. | Epoxy | Vyncolit® |
| Fainplast PVC PH 82/A | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Egyeuroptene PP 9003 | Egyptian European Company | PP Homopolymer | Egyeuroptene |
| KOCETAL® EL302BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Sylvin 8375-87C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |