DOW™ HDPE DGDC-2100 NT 7
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lit4kP_DOW-HDPE-DGDC-2100-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DOW DGDC-2100 NT 7 High Density Polyethylene Resin is a high-molecular weight, high-density film grade resin. This product was specifically designed to offer an optimal balance of physical properties and processability. DGDC-2100 NT7 HDPE resin is ideally suited for use in making grocery sacks, consumer and institutional liners, and merchandise bags. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.070 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 9.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 13 | µm | |
| Film Puncture Energy (13 µm) | 0.893 | J | Internal method |
| Film Puncture Force (13 µm) | 29.8 | N | Internal method |
| Film Puncture Resistance (13 µm) | 10.6 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 13 µm | 966 | MPa | ASTM D882 |
| 2% secant, TD : 13 µm | 1100 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 13 µm | 42.4 | MPa | ASTM D882 |
| TD : Yield, 13 µm | 31.8 | MPa | ASTM D882 |
| MD : Broken, 13 µm | 93.4 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 68.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 13 µm | 330 | % | ASTM D882 |
| TD : Broken, 13 µm | 410 | % | ASTM D882 |
| Dart Drop Impact (13 µm) | 350 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm | 11 | g | ASTM D1922 |
| TD : 13 µm | 73 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 128 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 12.7 µm) | 9 | ASTM D2457 | |
| Haze (12.7 µm) | 69 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：1.97 英寸 (50mm)；24:1 L/D 熔体温度：410 °F (210 °C) 输出：模具周长的 8 磅/小时/英寸 模具直径：3.94 英寸 (100mm) 放大比：4:1 内缩高度：32 英寸 (813 mm) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LXR515T | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Sylvin 8691-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen RP241G | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Trovidur® W 1014 | Röchling Engineering Plastics SE & Co. KG | PVC, Flexible | Trovidur® |
| APEX® 1835 | Teknor Apex Company | PVC, Flexible | APEX® |