HIPTEN® 22006
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | HIP-PetroHemija |
| Trademark: | HIPTEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lirUSe_HIPTEN-22006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIPTEN® 22006 is low density polyethylene resin developed for production of shrink film and extrusion of flexible pipes. Applications: Production of shrink film, flexible pipes. HIPTEN® 22006 has Health Certificate issued by Institute for Health Protection of Serbia. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 10.0 | MPa | ISO 527-2 |
| Fracture | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 600 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ISO 1184 | ||
| TD : Yield, 40 µm | 11.0 | MPa | ISO 1184 |
| MD : Break, 40 µm | 24.0 | MPa | ISO 1184 |
| TD : Break, 40 µm | 22.0 | MPa | ISO 1184 |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 40 µm | 350 | % | ISO 1184 |
| TD : Break, 40 µm | 600 | % | ISO 1184 |
| Dart Drop Impact (40 µm) | 150 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 40.0 µm | 135.1 | kN/m | ASTM D1922 |
| TD : 40.0 µm | 173.7 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 200 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 2:1 to 3 : 1 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNILID 1256 | Tekni-Films, a div of Tekni-Plex | Film, Coated Al Foil | TEKNILID |
| Westlake LDPE EF677 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| AIE PA66 60G6ST | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| KYOCERA KE-200DH | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| Karina BLACK PVC COMPOUND 750-48/1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |