ELEVATE™ EB508AA
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | ELEVATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | li4tNb_ELEVATEEB508AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake ELEVATE™ EB508AA is an ethylene vinyl acetate copolymer with 18% VA. EB508AA is designed for flexible packaging and other films that require excellent toughness and good heat sealing characteristics. This resin has excellent low temperature brittleness properties, melt strength, and flexibility. Application/Uses
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 51 µm, blown film | 51.7 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm, blown film | 58.6 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 31.7 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 31.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 950 | % | ASTM D882 |
| Dart Drop Impact (51 µm, Blown Film) | 600 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 67.8 | °C | ASTM D1525 |
| Peak Melting Temperature | 86.1 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm, Blown Film) | 85 | ASTM D2457 | |
| Haze (50.8 µm, Blown Film) | 2.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 2.0 mils; blow up ratio 2.5:1; die gap 35 mils. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 199 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE PCG80063 | SABIC Americas, Inc. | HDPE | SABIC® HDPE |
| Quantum Composites QC-8600FR | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| FERREX® GPP40CC47HB | Ferro Corporation | PP Homopolymer | FERREX® |
| KumhoSunny ABS 720 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| LNP™ LUBRICOMP™ RL002 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |