Impet® 830R
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Impet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lgbWov_Impet-830R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impet 830R is a 35% glass/mineral reinforced injection moldable polyester made with recycled PET. It provides an excellent combination of strength, stiffness, warp resistance, and high temperature capability together with excellent processability (high flow) during molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.60 | g/cm³ | ASTM D792 |
| -- | 1.59 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.60 | % | ISO 294-4 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.13 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 103 | MPa | ASTM D638 |
| Fracture | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.1 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 10900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.3 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 22 | kJ/m² | ISO 179/1eU |
| 23°C | 26 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 6.4 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 216 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 206 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 76.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 244 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | |||
| -- | 1.0E+15 | ohms·cm | ASTM D257 |
| -- | 7.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength 3 | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (10 kHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (10 kHz) | 0.016 | ASTM D150 | |
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index | |||
| -- | 200 | V | IEC 60112 |
| -- | 175 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 255 - 265 | °C | |
| Middle Temperature | 260 - 275 | °C | |
| Front Temperature | 260 - 275 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 110 - 121 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 260 to 290°CZone 4 Temperature: 265 to 280°CFeed Temperature: 255 to 265°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PS 3122 (UK) | MBA Polymers | PS (GPPS) | MBA PS |
| Stylac™ IX600 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| VENELENE® FA-0240 | Poliolefinas Internacionales, C.A. (Polinter) | LDPE | VENELENE® |
| LUVOCOM® 1850-7795 VP | Lehmann & Voss & Co. | PBT | LUVOCOM® |
| Sylvin 8250-80FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |