Zytel® PLUS PLS90G30DR BK099
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® PLUS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lgSXxy_ZytelPLUSPLS90G30DRBK099.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Hydrolysis Resistant, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.90 | -- | % | ISO 294-4 |
| Flow | 0.20 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C, 2.00mm | 6.0 | -- | % | ISO 62 |
| Balance, 23°C, 2.00mm, 50% RH | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 190 | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 5.8 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 252 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 263 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification (1.5 mm) | HB | -- | IEC 60695-11-10, -20 | |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 290 | °C | |
| Mold Temperature, Optimum | 100 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Ejection Temperature | 210 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 70 - 120 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9996-78 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| YUNTIANHUA® ST-10 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNTIANHUA® |
| ICORENE® N6601 | ICO Polymers EMEA, A Division of A. Schulman | ABS | ICORENE® |
| LUVOCOM® 1-8259 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| CP PRYME® ABS A100-89 | Chase Plastics Services Inc. | ABS | CP PRYME® ABS |