Stat-Rite® M690
| Category: | PETG , Polyethylene Terephthalate Glycol Comonomer |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Stat-Rite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lgMcxo_Stat-Rite-M690.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Rite® M690 is a static dissipative PETG alloy. Stat-Rite M690 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protection. Stat-Rite® IDP alloys provide consistent static dissipation even when extruded, injection molded or thermoformed into components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1240 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 1100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 60.0 | °C | |
| 1.8 MPa, Unannealed | 55.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- 1 | 2.0E+9 | ohms | ESD S11.11 |
| -- 2 | 2.0E+10 | ohms | ASTM D257 |
| Volume Resistivity | 2.0E+10 | ohms·cm | ASTM D257 |
| Static Decay 3 | |||
| +5000 V to 50 V | 0.1 | sec | |
| -5000 V to -50 V | 0.1 | sec | |
| Tribocharge - Nitrile Glove | 25.0 | V | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ionic Content | Internal Method | ||
| Anions Cl- | 20.0 | ng/cm² | |
| Anions NO3- | 30.0 | ng/cm² | |
| Anions PO4- | 40.0 | ng/cm² | |
| Anions SO4- | 10.0 | ng/cm² | |
| Cations Na+ | 150 | ng/cm² | |
| Non-Volatile Content | 1.00 | µg/cm² | Internal Method |
| Outgassing | Internal Method | ||
| MMA | 0.250 | µg/g | |
| Styrene | 0.0300 | µg/g | |
| Toluene | 0.0500 | µg/g | |
| Total Organics | 1.70 | µg/g |
| Note Message | |
|---|---|
| 1 . | 12% RH |
| 2 . | 50% RH |
| 3 . | FTMS-101C, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier LH01019 - A | Premier Polymers, LLC. | LLDPE | Premier |
| Toyolac® 100 X01 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Badamid® LA70 GF25 | Bada AG | Nylon 66 | Badamid® |
| Adsyl 5 C 37 F ST | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| LNP™ THERMOTUF™ VF004S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |