TOTAL Polypropylene PPH 3480Z
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lfzk0c_TOTAL-Polypropylene-PPH-3480Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polypropylene 3480Z is formulated specifically to give excellent process stability in high profile extrusion. Low catalyst residues in TOTAL Polypropylene 3480Z provide outstanding color, plus low taste and odor. TOTAL Polypropylene 3480Z is formulated to minimize surface static build-up. TOTAL Polypropylene 3480Z complies with all applicable FDA regulations for food contact applications. TOTAL Polypropylene 3480Z is recommended for high speed profile extrusion for standard and flexible drinking straws. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.8 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 | |
| Durometer Hardness (Shore D) | 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1520 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 36.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 10 | % | ASTM D638 |
| Fracture | 100 | % | ASTM D638 |
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 107 | °C | ASTM D648 |
| Melting Temperature | 166 | °C | DSC |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Elongation at Break, ASTM D638: >100% |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 232 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 211 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| EMPILON® 755 | EMPILON | SEBS | EMPILON® |
| HiFill® PEEK GF15 HF | Techmer Engineered Solutions | PEEK | HiFill® |
| Hostalen PP H2150 304850 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |
| ALTECH® PA6 ECO 4240/106 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |