Larton G/40 I6
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Larton |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lfBcxl_Larton-G-40-I6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyphenylene Sulphide (PPS) based compound. Glass fibres. Intrinsically flame retardant. Good elongation. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 1.1 | % | |
| Flow : 2.00 mm | 0.15 to 0.45 | % | |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 15000 | MPa | |
| 60°C | 14500 | MPa | |
| 90°C | 14000 | MPa | |
| 120°C | 9200 | MPa | |
| 150°C | 6000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 195 | MPa | |
| Break, 60°C | 180 | MPa | |
| Break, 90°C | 150 | MPa | |
| Break, 120°C | 110 | MPa | |
| Break, 150°C | 85.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.7 | % | |
| Break, 60°C | 1.7 | % | |
| Break, 90°C | 2.6 | % | |
| Break, 120°C | 3.0 | % | |
| Break, 150°C | 3.3 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 280 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 260 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 220 | °C | |
| Vicat Softening Temperature | 260 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 6.0E-6 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 44 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 130 to 140 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNPRENE® FE65HB | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNPRENE® |
| TOTAL Polypropylene PPC 13442 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Flontech® FT-915-RSL | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Latan 13 K/30 | LATI S.p.A. | Acetal (POM) Copolymer | Latan |
| Karina IVORY PVC COMPOUND -E 854-35/ 1-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |