POLYFLAM® RPP 60335 CS1 5V
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lf3i8X_POLYFLAM-RPP-60335-CS1-5V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% mineral filled flame-retardant PP-Homopolymer; without PBDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 2.5 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 10 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 101 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 58.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 85.0 | °C | ISO 306/B50 |
| Ball Pressure Test (130°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | UL 746 | ||
| 0.750 mm | 65.0 | °C | UL 746 |
| 1.50 mm | 65.0 | °C | UL 746 |
| 2.00 mm | 65.0 | °C | UL 746 |
| 3.00 mm | 65.0 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.750 mm | 65.0 | °C | UL 746 |
| 1.50 mm | 65.0 | °C | UL 746 |
| 2.00 mm | 65.0 | °C | UL 746 |
| 3.00 mm | 65.0 | °C | UL 746 |
| RTI | UL 746 | ||
| 0.750 mm | 65.0 | °C | UL 746 |
| 1.50 mm | 65.0 | °C | UL 746 |
| 2.00 mm | 65.0 | °C | UL 746 |
| 3.00 mm | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ISO 3795 | ||
| 0.750mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 1.50mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 3.00mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.750 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.50 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-0 5VB | UL 94, IEC 60695-11-10, -20 | |
| 2.00 mm | 5VB | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 800 | °C | IEC 60695-2-13 |
| 1.50 mm | 800 | °C | IEC 60695-2-13 |
| 3.00 mm | 800 | °C | IEC 60695-2-13 |
| Oxygen Index | 35 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP5610 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| VITAMIDE® AS10VN6543 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Vipel® K022-CCL-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| Celcon® LU02 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Laticonther 57 CPG/550 | LATI S.p.A. | PPA | Laticonther |