Sasol Polymers PP HKR102

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	Sasol Polymers
Trademark:	Sasol Polymers PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lenGeA_Sasol-Polymers-PP-HKR102.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features

Low flow

Low water carry over during the extrusion process

Suitable for high strength technical articles requiring superior mechanical properties

Available in narrow viscosity range (HKQ102)

Applications
Extrusion

Woven industrial fabric for high strength products

Carpet backing

Sacks and bags

Flexible intermediate bulk containers (FIBC's)

Monofilaments

Packaging strapping

Injection moulding

Domestic, industrial and general purpose articles

General Information
Additive	Processing stabilizer
Features	High strength Homopolymer Good processing stability Low liquidity Compliance of Food Exposure Low water portability
Uses	Bags monofilament Carpet backing Industrial application Household goods Belt material Container General Fabric
Agency Ratings	EC 1935/2004 FDA 21 CFR 177.1520(a)(3)(i)(c)(1) FDA 21 CFR 177.1520(c) 3.1a
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	3.5	g/10 min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction	1.4	%	ISO 294-4
Flow direction	1.5	%	ISO 294-4

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	72.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1600	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	34.5	MPa	ISO 527-2/1A/50
Tensile Strain			ISO 527-2/1A/50
Yield	9.0	%	ISO 527-2/1A/50
Fracture	> 50	%	ISO 527-2/1A/50
Flexural Modulus	1550	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.5	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	85.0	°C	ISO 75-2/B
1.8 MPa, not annealed	53.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	154	°C	ISO 306/A120
--	90.0	°C	ISO 306/B120
Melting Temperature	163	°C	ISO 11357-3

Injection	Nominal Value	Unit
Hopper Temperature	40.0 - 60.0	°C
Rear Temperature	180 - 260	°C
Middle Temperature	220 - 280	°C
Front Temperature	240 - 280	°C
Nozzle Temperature	220 - 280	°C
Processing (Melt) Temp	220 - 280	°C
Mold Temperature	20.0 - 60.0	°C

Injection instructions
Zone 4: 240 to 280°C

Extrusion	Nominal Value	Unit
Hopper Temperature	40.0 - 60.0	°C
Cylinder Zone 1 Temp.	220 - 280	°C
Cylinder Zone 2 Temp.	240 - 280	°C
Cylinder Zone 3 Temp.	240 - 280	°C
Cylinder Zone 4 Temp.	240 - 280	°C
Cylinder Zone 5 Temp.	240 - 280	°C
Melt Temperature	220 - 280	°C
Die Temperature	240 - 260	°C

Resin Grade	Manufacturer	Category	Trademark
Sinpolene MBB1782	Teknor Apex Asia Pacific PTE. LTD.	PE, Unspecified	Sinpolene
TEKANATE™ G7010	Mando Advanced Materials Co., Ltd.	PC	TEKANATE™
Monprene® MP-1852	Teknor Apex Company	TPE	Monprene®
Witcom PPS 2007/277	Witcom Engineering Plastics B.V.	PPS	Witcom PPS
LNP™ STAT-LOY™ A3000 compound	SABIC Innovative Plastics	ABS	LNP™ STAT-LOY™