Order Products : sales@su-jiao.com
Badatron® PPS CF20
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Bada AG |
| Trademark: | Badatron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lemFCn_BadatronPPSCF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High strength PPS injection moulding grade , 20% carbon fibers, good electrical conductivity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.39 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 18000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 170 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.0 | % | ISO 527-2/5 |
| Flexural Stress 1(23°C, 4.00 mm) | 240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 2(23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) 3 | 295 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 4(1.00 mm) | < 1.0E+3 | ohms | IEC 60093 |
| Volume Resistivity 5(1.00 mm) | < 1.0E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.8 mm | V-0 | UL 94 | |
| 1.6 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 310 - 340 | °C | |
| Mold Temperature | 130 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | 80x10x4 mm |
| 2 . | 80x10x4 mm |
| 3 . | Compound for molding, 10k/min |
| 4 . | 80x80x1 mm |
| 5 . | 80x80x1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SARANEX™ 14P | The Dow Chemical Company | PVDC | SARANEX™ |
| Ultrason® E KR 4113 | BASF Corporation | PESU | Ultrason® E |
| LNP™ THERMOCOMP™ RF008XXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Sumiliteresin® PR-50064 I | SBHPP | Phenolic | Sumiliteresin® |
| Sylvin 86032-90 Clear 8443 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |