TECOLITE KM-36C
| Category: | Phenolic , Phenolic |
| Manufacturer: | KYOCERA Chemical Corporation |
| Trademark: | TECOLITE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lcs7Bk_TECOLITE-KM-36C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Good moldability and Good productivity. Provides suitable compounds and Superior cost performance. Kyocera Chemical's Phenolic Molding Compounds "TECOLITE" have a good high voltage resistance and a good moldability. "TECOLITE" are designed for insulation boards and telecommunication parts. Moreover coloring compounds are possible. Therefore can select the most suitable compounds for parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | |
| Molding Shrinkage - Flow 1 | 0.70 to 0.90 | % | |
| Water Absorption (Equilibrium) | < 0.30 | % |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Flexural Strength | 88.0 to 108 | MPa |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Deflection Temperature | 165 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | |||
| After Boiling | 1.0E+8 to 1.0E+9 | ohms | |
| As Molded | 1.0E+9 to 1.0E+10 | ohms | |
| Dielectric Strength | > 8.0 | kV/mm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Compression Molding |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2950 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 2103 TFE 10 | RTP Company | PEI | RTP |
| RTP 4085 TFE 10 | RTP Company | PPA | RTP |
| Sylvin 9639-83AM Clear 8354 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unichem 8711A-02 | Colorite Polymers | PVC, Unspecified | Unichem |