SABIC® LDPE 2501N0 Datasheet,LDPE,Saudi Basic Industries Corporation (SABIC)-SHANGHAI SUSHENG

Message
SABIC® LDPE 2501N0 is a grade without additives with a low gel level, which combines good draw down ability with fair optical properties and stiffness. Application Blown Film: SABIC® LDPE 2501N0 is typically used in diaper film, surface protection film, lamination film and in applications where low blocking behaviour is required and the presence of slip and anti block is unwanted. Cast Film: SABIC® LDPE 2501N0 is typically used in diaper film, lamination film and in applications where low blocking behaviour without the help of additives is required. This product is not intended for and must not be used in any pharmaceutical/medical applications.

General Information
Features	Low density Low speed solidification crystal point Rigid, good Optical Good stripping
Uses	Blown Film Laminate cast film
Processing Method	Lamination method Blow film cast film

Physical	Nominal Value	Unit	Test Method
Density	0.925	g/cm³	ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.75	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)	0.90		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested
-- ¹	25	µm
-- ²	50	µm
Elastic Modulus - MD (50 µm, Blown Film)	200	MPa	ASTM D882
Elastic Modulus - TD (50 µm, Blown Film)	200	MPa	ASTM D882
Tensile Modulus			ISO 527-3
MD : 25 µm, cast film	150	MPa	ISO 527-3
TD : 25 µm, cast film	160	MPa	ISO 527-3
Tensile Strength
MD : Yield, 50 µm, blown film	12.0	MPa	ASTM D882
TD : Yield, 50 µm, blown film	12.0	MPa	ASTM D882
MD : Yield, 25 µm, cast film	10.0	MPa	ISO 527-3
TD : Yield, 25 µm, cast film	9.00	MPa	ISO 527-3
MD : Broken, 50 µm, blown film	25.0	MPa	ASTM D882
TD : Broken, 50 µm, blown film	20.0	MPa	ASTM D882
MD : Fracture, 25 µm, cast film	28.0	MPa	ISO 527-3
TD : Fracture, 25 µm, cast film	18.0	MPa	ISO 527-3
Tensile Elongation
MD : Broken, 50 µm, blown film	> 200	%	ASTM D882
TD : Broken, 50 µm, blown film	> 500	%	ASTM D882
MD : Fracture, 25 µm, cast film	160	%	ISO 527-3
TD : Fracture, 25 µm, cast film	580	%	ISO 527-3

Impact	Nominal Value	Unit	Test Method
Impact Strength			ASTM D4272
Blown Film : 50.0 µm	150	J/cm	ASTM D4272
Cast Film : 25.0 µm	140	J/cm	ASTM D4272

Additional Information	Nominal Value	Unit	Test Method
Blocking - Blown Film (50.0 µm)	20	g	Internal method
Re-blocking - Blown Film (50.0 µm)		g	Internal method
Tear Strength ³			ISO 6383-2
MD : 50.0 µm	45.0	kN/m	ISO 6383-2
TD : 50.0 µm	45.0	kN/m	ISO 6383-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	98.0	°C	ISO 306/A

Optical	Nominal Value	Unit	Test Method
Haze			ASTM D1003A
50.0 µm, blown film	10	%	ASTM D1003A
25.0 µm, cast film	5.8	%	ASTM D1003A

Additional Information	Nominal Value	Unit	Test Method
Blown FilmFilm properties have been measured at film of 50 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm.Cast FilmThe optical and film properties are determined on 25 µm cast film. Die gap 1.0 mm.

Category:	LDPE , Low Density Polyethylene
Manufacturer:	Saudi Basic Industries Corporation (SABIC)
Trademark:	SABIC® LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lcOCZu_SABIC-LDPE-2501N0.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SABIC® PPcompound 7540	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
Telcar® SGI 70076	Teknor Apex Asia Pacific PTE. LTD.	TPE	Telcar®
UNITIKA Nylon 6 A1030JR	UNITIKA Plastics Division	Nylon 6	UNITIKA Nylon 6
Huafon JF-P-8370AD / JF-I-5218	Huafon Group Co., Ltd.	PUR-Ester	Huafon
Multilon® RN-7740M	TEIJIN LIMITED	PC+ABS	Multilon®