LNP™ STAT-KON™ 9X02785 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lc6gnN_LNP-STAT-KON-9X02785-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* 9X02785 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-D-02785 Product reorder name: 9X02785 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.27 | g/cm³ | |
| -- | 1.26 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.70 | % | |
| Across Flow : 24 hr | 0.50 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.091 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2850 | MPa | ASTM D638 |
| -- | 2760 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 64.1 | MPa | ASTM D638 |
| Yield 2 | 63.0 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/5 |
| Break 3 | 52.0 | MPa | ASTM D638 |
| Break | 52.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.3 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2/5 |
| Break | 4.0 | % | ASTM D638 |
| Break 5 | 7.8 | % | ASTM D638 |
| Break | 3.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2920 | MPa | ASTM D790 |
| -- | 2900 | MPa | ASTM D790 |
| -- 7 | 2800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 103 | MPa | ASTM D790 |
| -- | 96.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 107 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 75.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 60 | J/m | ASTM D256 |
| 23°C 10 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2200 | J/m | ASTM D4812 |
| 23°C 11 | 150 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 35.7 | J | ASTM D3763 |
| -- | 35.4 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 117 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 114 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 106 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 103 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+7 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP521-372 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| APEX® 2090-H | Teknor Apex Company | PVC, Flexible | APEX® |
| GAPEX® RPP20EB61HB NATURAL | Ferro Corporation | PP Homopolymer | GAPEX® |
| OmniLon™ PA6/6 GR23 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Petrothene® Select GS707061 | LyondellBasell Industries | LLDPE | Petrothene® Select |