Plenco 06527 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lc4CmK_Plenco-06527-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 06527 is a woodflour and mineral filled resole phenolic molding compound. It is available in brown. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Apparent Density | 0.59 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.27 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.35 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 56 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10600 | MPa | ASTM D638 |
| Tensile Strength | 52.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 8450 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Compressive Strength | 143 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 24.3 | J/m | ASTM D256 |
| Notched Izod Impact | 26 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 216 | °C | ASTM D648 |
| Continuous Use Temperature | 188 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.2E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 9.3 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 6.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.069 | ASTM D150 | |
| Arc Resistance | 162 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 34 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.26%Drop Ball Impact, PLENCO Method: 157 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F500EP (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| TOYOBO PPS TS101 | TOYOBO America, Inc. | PPS | TOYOBO PPS |
| Braskem PP R7051-10N | Braskem Europe GmbH | PP Random Copolymer | Braskem PP |
| Ferro PP NPP00GT20NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Elastamax™ XL-2055 | PolyOne Corporation | TPO (POE) | Elastamax™ |