Capran® 2500T Datasheet,Nylon 6,Honeywell-SHANGHAI SUSHENG

Message
CAPRAN® 2500 is a 1.0 mil (25 micron) biaxially oriented nylon 6 film with excellent flex crack resistance and superior clarity properties well suited for packaging applications requiring excellent mechanical strength.

General Information
Features	High strength Good cracking resistance Definition, high Barrier resin
Uses	Bi-axially Oriented Film Packaging
Forms	Films

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With Metal-Dynamic	0.23	ASTM D1894
With self-dynamics	0.70	ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
secant modulus			ASTM D882
MD : 25 µm	2760	MPa	ASTM D882
TD : 25 µm	2760	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Break, 25 µm	262	MPa	ASTM D882
TD : Break, 25 µm	262	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 25 µm	90	%	ASTM D882
TD : Break, 25 µm	90	%	ASTM D882
Oxygen Permeability (23°C, 25 µm)	0.71	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission Rate (25 µm, 38°C, 100% RH)	190	g·mm/m²/atm/24 hr	ASTM F1249

Optical	Nominal Value	Unit	Test Method
Gloss (20°, 25.4 µm)	90 - 140		ASTM D2457
Haze (25.4 µm)	2.3 - 3.4	%	ASTM D1003

Additional Information
Yield: 24000 in²/lbTensile Strength @ Break, ASTM D 882, MD: 34000 to 42000 psiTensile Strength @ Break, ASTM D 882, TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD: 70 to 90%Elongation @ Break, ASTM 882, TD: 70 to 90%Secant Modulus, ASTM D 882, MD: 350000 to 450000 psiSecant Modulus, ASTM D 882, TD: 350000 to 450000 psiGraves Tear (initial), ASTM D 1004, MD: 1100 to1500 g/milGraves Tear (initial), ASTM D 1004, TD: 1000 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 0.2 to 0.7% shrinkageWater Vapor Transmission ASTM F1249, 100°F, 100%RH: 11 to 13 g/100 in²/dayOxygen Transmission Rate, ASTM D, 77°F, 0%RH: 1.3 to 2.3 cc/100 in²/day

Additional Information

Yield: 24000 in²/lbTensile Strength @ Break, ASTM D 882, MD: 34000 to 42000 psiTensile Strength @ Break, ASTM D 882, TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD: 70 to 90%Elongation @ Break, ASTM 882, TD: 70 to 90%Secant Modulus, ASTM D 882, MD: 350000 to 450000 psiSecant Modulus, ASTM D 882, TD: 350000 to 450000 psiGraves Tear (initial), ASTM D 1004, MD: 1100 to1500 g/milGraves Tear (initial), ASTM D 1004, TD: 1000 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 0.2 to 0.7% shrinkageWater Vapor Transmission ASTM F1249, 100°F, 100%RH: 11 to 13 g/100 in²/dayOxygen Transmission Rate, ASTM D, 77°F, 0%RH: 1.3 to 2.3 cc/100 in²/day

Resin Grade	Manufacturer	Category	Trademark
Tarnamid® T-27 GF 115	Grupa Azoty S.A.	Nylon 6	Tarnamid®
Braskem PP C791-30NA	Braskem Europe GmbH	PP Impact Copolymer	Braskem PP
Capilene® T 12 EV	Carmel Olefins Ltd.	PP Homopolymer	Capilene®
Karina BLACK PVC COMPOUND 807D48/1-D-IS-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
ESTOPLAST EP 4030WW01	Ester Industries Ltd.	PBT	ESTOPLAST EP

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Honeywell
Trademark:	Capran®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lbotrE_Capran-2500T.pdf
PRICE:	Order Products email sales@su-jiao.com