| Category: | PSU , Polysulfone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Lasulf |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lbnoxN_Lasulf-LASULF-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polysulphone (PSU). UL94 V-0 classified, halogens free. Glass fibres. Low smoke toxicity index and optical density. Very high dimensional stability. Low thermal expansion coefficient. Very high thermal resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.45 to 0.60 | % | |
| Flow : 2.00 mm | 0.10 to 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 8000 | MPa | |
| 60°C | 7700 | MPa | |
| 90°C | 7500 | MPa | |
| 120°C | 7300 | MPa | |
| 150°C | 7000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 135 | MPa | |
| Break, 60°C | 130 | MPa | |
| Break, 90°C | 115 | MPa | |
| Break, 120°C | 105 | MPa | |
| Break, 150°C | 90.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.7 | % | |
| Break, 60°C | 2.5 | % | |
| Break, 90°C | 2.4 | % | |
| Break, 120°C | 2.2 | % | |
| Break, 150°C | 2.1 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 70 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 190 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 160 | °C | |
| Vicat Softening Temperature | 185 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 6.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Oxygen Index | 38 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 300 to 330 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2281 HF | RTP Company | PEEK | RTP |
| Fainplast PVC KL 97 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Eltex® P HCW280 | INEOS Olefins & Polymers Europe | PP Homopolymer | Eltex® P |
| Kepital® F10-03HT | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Huaxia Shenzhou FKM 246G | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |